Casting-Bars
2A12 aluminum rod
High-strength duralumin, which can be strengthened by heat treatment, and can be welded
Grade | Old brand | Si | Fe | Cu | Mn | Mg | Cr | Zn | Ti | Zr | Add element | other | Al | |
single | total | |||||||||||||
2A12 | LY12 | 0.50 | 0.50 | 3.8-4.9 | 0.30-0.90 | 1.2-1.8 | — | 0.30 | 0.15 | — | Ni0.10 Fe+Ni0.50 | 0.05 | 0.15 | margin |
Typical uses Typical use
2A12use mainly for the production of various parts and high-load member (but not including stamping forging) as a skeleton on the plane part, skin, bulkheads, ribs, spars, such as rivets150or less ℃ Work parts.
Quality Characteristics Quality Characteristics
Density:2.80 g / cmł. Poisson's ratio:0.33at20°C (68°F). Elastic modulus: Tensile:72.4GPa(10.5 × 10. 6PSI) Shear:28.0GPa(4.0 × 10. 6PSI) pressurereduction:73.8GPa(10.7 × 10. 6PSI)
Grade | state | Diameter (square rod and hexagonal rod refer to the diameter of the inscribed circle)/mm | Tensile strength Rm/Mpa | Yield strength Rp0.2/Mpa | Elongation/% | Bending radius α | |||||
A5.65 | A50mm | 180° | 90° | ||||||||
not less than | |||||||||||
2A12 | O | — | ≤245 | — | 12 | 10 | |||||
T4 T42 |
≤5.0 | 390 | 295 | — | 8 | — | — | ||||
>5.0~10.0 | 410 | 295 | — | 8 | — | — | |||||
>10.0~20.0 | 420 | 305 | 10 | — | — | — | |||||
>20.0~150.0 | 420 | 255 | 12 | — | — | — |
6082 aluminum rod
Excellent weldability, corrosion resistance, formability and machinability
Alloy 6082 combines excellent weldability, brazing properties, corrosion resistance, formability and machinability. The -0 and T4 states of alloy 6082 are suitable for bending and forming occasions, and the -T5 and -T6 states are suitable for the requirements of good machinability. Some specific processing requires the use of chip separators or other special processes to help separate the chips; 6082 Alloys usually have good processing characteristics and good anode reaction performance;
Grade | Old brand | Si | Fe | Cu | Mn | Mg | Cr | Zn | Ti | Zr | Add element | other | Al | |
single | total | |||||||||||||
6082 | — | 0.7-1.3 | 0.50 | 0.10 | 0.40-1.0 | 0.6-1.2 | 0.25 | 0.20 | 0.10 | — | — | 0.05 | 0.15 | margin |
Typical uses Typical use
6082are widely used, trucks, other needs have strength, aviation fixture tower buildings, ships, pipes and the weldability and corrosion resistance of building applications. Such as: aircraft parts, camera lenses, couplers, marine accessories and hardware, electronic accessories and connectors, decorative or various hardware, hinge heads, magnetic heads, brake pistons, hydraulic pistons, electrical accessories, valves and valve parts.
Quality Characteristics Quality Characteristics
Density:2.85g / cmł.
Hardness:Ostate:40HB;T4,T451state:58HB;T6, T651state:90HB; the data is taken fromthe test results of a10mmdiameterball and30sunder a load of500kg.
Grade | state | Diameter (square rod and hexagonal rod refer to the diameter of the inscribed circle)/mm | Tensile strength Rm/Mpa | Yield strength Rp0.2/Mpa | Elongation/% | Bending radius α | Hardness / HBW α | |||||
A5.65 | A50mm | 180° | 90° | |||||||||
not less than | ||||||||||||
6082 | 0, H111 | ≤200 | ≤160 | ≤110 | 14 | 12 | — | — | — | |||
T4 | ≤200 | 205 | 110 | 14 | 12 | — | — | — | ||||
T6 | ≤20 | 295 | 250 | 8 | 6 | — | — | — | ||||
>20~150 | 310 | 260 | 8 | — | — | — | — | |||||
>150~200 | 280 | 240 | 6 | — | — | — | — | |||||
>200~250 | 270 | 200 | 6 | — | — | — | — |
Contact information
Recommended
Product center
+86-591-22277633
Time:08:00-17:00
sales@metal-new.com
Looking forward to receiving your email
Message
Looking forward to receiving your message
Wuhushan Industry Area, Qingkou Investment Zone, Fuzhou, Fujian, China Contacter:Mr Ke
Join our Newsletter